Alloy |
Temper |
Tensile
Strength
ksi
|
Yield
Strength
ksi
|
Minimum
Elongation in
2" (%) |
Rockwell
(1)
Hardness
|
|
304
304L
|
Annealed
Half Hard
Full Hard
|
100
max.
110-140
140 min.
|
25-45
70-110
110 min.
|
35
15
7
|
B
90 max.
B 93-C 30
C 22 min.
|
|
| 310 |
Annealed
Half Hard
Full Hard |
100
max.
115-135
140 min. |
35-55
75-115
115 min. |
35
15
5 |
B
95 max.
B 95-C 26
C 24 min. |
|
316
316L
|
Annealed
Half Hard
Full Hard |
100
max.
110-140
140 min. |
30-50
70-110
110 min. |
35
15
6 |
B
95 max.
B 95-C 26
C 24 min. |
|
| 321 |
Annealed
Half Hard
Full Hard |
100
max.
110-140
140 min. |
35-55
80-120
120 min. |
35
15
6 |
B
92 max.
B 95-C 26
C 24 min. |
|
| 347 |
Annealed
Half Hard
Full Hard |
100
max.
110-140
140 min. |
35-55
80-120
120 min. |
35
15
6 |
B
92 max.
B 95-C 26
C 24 min. |
|
403
410
|
Annealed
Half Hard
Full Hard |
85
max.
85-100
100 min. |
30-50
65-85
85 min. |
35
15
5 |
B
95 max.
B 90-B 100
C 96 min. |
|
| 430 |
Annealed
Half Hard
Full Hard |
85
max.
82-97
98 min. |
35-50
60-90
85 min. |
35
15
5 |
B
90 max.
B 85-98
C 93 min. |
|
| 446 |
Annealed
Half Hard
Full Hard |
95
max.
95-115
115 min. |
40-75
70-90
85 min. |
35
15
4 |
B
95 max.
B 90-C 24
B 96 min. |
|
| A-286 |
Annealed
Half Hard
Full Hard |
1010
max.
115-140
140 min. |
35-65
80-110
110 min. |
35
15
3 |
B
95 max.
B 96-C 26
C 26 min. |
|